TC11钛合金在疲劳-蠕变交互作用下的解理断裂研究

周煜 , 周义刚 , 俞汉清

金属学报

研究了具有等轴、双态和网篮三种组织的TC11合金在520℃下的疲劳—蠕变交互作用特性,发现在断裂过程中出现的解理特征不仅与蠕变空洞形核率有关,而且受拉伸保时过程中裂尖蠕变应变累积和裂尖应力状态的控制,即受临界空洞形核应变和临界空穴扩张比参数V_(GC)的综合影响。

关键词: 疲劳—蠕变交互作用 , cleavage rupture , void initiation , void growth , TC11 Ti alloy

EQUIAXED REFINEMENT OF GRAINS IN ALLOY TC11

SU Zuwu MENG Guowen GUO Hongzhen LIU Jianchao YAO Zekun Northwestern Polytechnical University , Xi'an , ChinaYANG Zhaosu HU Zongshi Baoji Non-Ferrous Metals Mill , Baoji , China

金属学报(英文版)

The formation reason and elimination method of non-uniform microstructure defects in Ti al- loy TC11 bar have been studied.The coagulating and coarsening into block of the part of grain boundary α and secondary α seem to be caused by the ingot cogging and initial forging temperature in the β region as well as no more enough deformation and uneven distribution. The grain α,elongated α and blocky α may be finally eliminated by adopting the technique of (α+β)thermomechanical processing+β processing,W.Q.+recrystallization annealing,A.C., thus the size of uniform and fine equiaxed α structure is believed to be reduced to 1.9258μm.

关键词: TC11 Ti alloy , null , null , null

钛合金片层组织两相区变形时的流动软化机理分析

宋鸿武张士宏程明李臻熙曹春晓包春玲

金属学报 doi:10.3724/SP.J.1037.2010.00534

钛合金片层组织在两相区变形时流动应力随应变的增加普遍表现为快速硬化和持续软化的特征. 为了研究该流动软化的机理, 采用等温热压缩实验研究了TC11合金片层组织在温度890-995 ℃和应变速率0.01-10 s^-1范围内的热变形行为. 理论计算表明α/β片层界面(α片层内孪晶界)产生的 Hall-Petch强化效应远大于片层束集边界. TC11合金片层组织高温变形的流动软化机理可归结为硬滑移模式向软滑移模式转变导致Hall-Petch强化效应的减弱.

关键词: TC11钛合金 , subtransus deformation , flow softening , Hall-Petch effect

TC11钛合金棒材显微组织等轴细晶化工艺研究

苏祖武 , 孟国文 , 郭鸿镇 , 刘建超 , 姚泽坤 , 杨昭苏 , 胡宗式

金属学报

本文对TC11钛合金棒材显微组织不均匀缺陷产生原因及消除途径进行了研究。结果表明,由于铸锭最初锻造温度在β相区,随后两相区锻造变形量不大且分布不均匀,致使部分晶界α和二次α聚集并粗化呈块状,或沿主变形方向拉长呈条状,或遗留下原晶界α。若采用(α+β)中间形变热处理+β处理、水冷+再结晶退火、空冷的工艺,可完全消除晶界α,拉长α和块状α相,获得均匀细小等轴α组织,初生等轴α相的平均直径可细化至1.9μm。

关键词: TC11钛合金 , forging , microstructure , equiaxed grain refinement